| Document |
Document Title |
|
JPH03150371A |
PURPOSE: To simply form a glass coating film on an article of iron-based stock without carrying out firing in a kiln by thermally spraying glaze on the stock heated to the softening start temp. of the glaze or above. CONSTITUTION: Iron-b...
|
|
JPH03138379A |
PURPOSE: To easily produce a porcelain enamel product of stone-like pattern having an external appearance close to that of natural stone by discharging plural glazes dissimilar in color to each other from glazing guns, respectively, into...
|
|
JPH0338333B2 |
|
|
JPH03130380A |
PURPOSE: To obtain the steel sheet excellent in adhesion without deteriorating its characteristic such as press formability and fish-scale resistance by hot-rolling and recrystallization-annealing a continuously cast slab with the compos...
|
|
JPH0334372B2 |
PURPOSE:To obtain a covered body having a self-cleaning covering layer having superior adhesion and contg. no crater in a process for forming an oxidation catalyst layer supported by a specified activated alumina on an Al plated steel sh...
|
|
JPH0334370B2 |
PURPOSE:To prevent penetration corrosion due to mist and to impart corrosion resistance for a long time in a cooking device by coating a first coating layer consisting essentially of water soluble silicate and a second coating layer cont...
|
|
JPH03111583A |
PURPOSE: To improve adhesive strength, wear resistance, and mechanical impact resistance while obviating the necessity of surface preparation by applying an inorganic coated film to a stainless steel in which respective contents of C, N,...
|
|
JPH03111582A |
PURPOSE: To improve adhesive strength, wear resistance, and mechanical impact resistance while obviating the necessity of surface preparation by applying ceramic coating to a stainless steel in which respective contents of C, N, Si, Cr, ...
|
|
JPH0327623B2 |
|
|
JPH0325515B2 |
|
|
JPH0379775A |
PURPOSE: To form a white coated body having superior heat resistance by using a coating prepd. by blending silicone resin with a borosiloxane resin, glass frit, titanium oxide, an alkaline earth metal oxide and a filler. CONSTITUTION: Si...
|
|
JPH0322461B2 |
A hot-rolled steel sheet suitable for enamelling on one side is disclosed. The steel consists essentially of 0.0050-0.07 wt % C, 0.05-1.5 wt % Mn, 0.03 0.15 wt % P, 0.03-0.1 wt % Al, 0.003-0.010 wt % N, provided that the N content is the...
|
|
JPH0356645A |
PURPOSE: To obtain the steel sheet for enamel having excellent enamel characteristics, such as foam and black spot detect resistance, by incorporating specific ratios of C, Mn, P, S, Al, N, Cu, Se, and Ti into the steel sheet, incorporat...
|
|
JPH0350169A |
PURPOSE: To efficiently and surely form a glass coating film without causing cracking by preheating the surface of a body to be coated to a specified temp., thermally spraying glass material on the preheated surface and slowly cooling th...
|
|
JPH0315722B2 |
A durable spandrel panel comprising a colored ceramic enamel coating protected by a transparent metal oxide film is disclosed, wherein the dominant wavelength of light reflected by the colored ceramic enamel coating is not equivalent to ...
|
|
JPH0347979A |
PURPOSE: To efficiently and surely form a glass coating film which is not peeled or cracked on the surface of a metal by blasting the surface, preheating the surface to a specified temp. and then thermally spraying a glass material on th...
|
|
JPH0313312B2 |
|
|
JPH0339458A |
PURPOSE: To obtain a clad material of metal and oxide superconductor excellent in adhesive strength to a metallic base material and free from peeling due to the deformation of the metallic base material by forming a coarse intermediate l...
|
|
JPH0339487A |
PURPOSE: To remove the borderline between a box mold and a personal ornament and to obtain films of the same color by polishing the surface of the box mold in which cloisonne is formed and the surface of the personal ornament, forming a ...
|
|
JPH0338093A |
PURPOSE: To improve the surface smoothness of an enamel substrate by coating a metallic substrate with amorphous glass and performing heat pressing on the substrate at a specific temperature after the substrate is fired at the working te...
|
|
JPH0331485A |
PURPOSE: To improve the surface smoothness of an enameled substrate for a thermal head by forming a glass film contg. filler made of fine particles of glass having a higher softening point than the glass of the glass film on a metal subs...
|
|
JPH0324283A |
PURPOSE: To easily form characters and patterns, etc., on an enamel layer on the surface of a metallic base material, by forming a mask layer for forming a display part of the characters and patterns, etc., then spraying superhard partic...
|
|
JPH036679B2 |
|
|
JPH036330A |
PURPOSE: To improve the porcelain enameling characteristics, deep drawability and weldability of the steel sheet by subjecting a slab of a steel having regulated amounts of N and contg. Ti particularly in the specified relationship with ...
|
|
JPH03106U |
|
|
JPH02149762U |
|
|
JPH02301574A |
PURPOSE: To render heat accumulating property to an enameled substrate by coating a metal substrate with two or more kinds of glasses having different compsns. by electrodeposition. CONSTITUTION: A metal substrate 1 is coated with two or...
|
|
JPH0246052Y2 |
|
|
JPH0257711B2 |
|
|
JPH0246051Y2 |
|
|
JPH02289478A |
PURPOSE: To prevent the damage of the surface by forming a transparent TiO2 layer on a material such as a ceramic material and irradiating with pulsed laser light to generate discoloration. CONSTITUTION: The transparent TiO2 layer having...
|
|
JPH0243508Y2 |
|
|
JPH0243507Y2 |
|
|
JPH02267286A |
PURPOSE: To obtain an enameled substrate whose coating layer has a smooth surface and superior characteristics as a substrate for a thermal head by forming an enamel layer on the surface of a metal substrate and a coating layer of glass ...
|
|
JPH02264699A |
PURPOSE: To enable reducing the coefficient of friction and also to prevent the whole front surface of a sole from being sensitive to dyeing by permitting the front surface to include embossing enamel strips which are substantially paral...
|
|
JPH0247555B2 |
|
|
JPH0247554B2 |
|
|
JPH0247552B2 |
|
|
JPH0247553B2 |
|
|
JPH02259087A |
PURPOSE: To prevent chipping and to easily and stably form a uniform thin coat by adhering a flexible base materiel to a powdery glass sheet with a sticky layer in-between and handling the reinforced powdery glass sheet. CONSTITUTION: A ...
|
|
JPH0237886Y2 |
|
|
JPH0245352B2 |
|
|
JPH0235807Y2 |
|
|
JPH0235808Y2 |
|
|
JPH02243782A |
PURPOSE: To easily recover a glaze and to dry-pattern an enameled casting by adding a paste to the fine powder of an inorg. material, granulating the mixture into coarse inorg. grains having specified diameter which are mixed into a dry ...
|
|
JPH02243580A |
PURPOSE: To improve the adhesiveness to ceramic surfaces by subjecting ceramic frit treated with a specific polysiloxane to hot or cold milling, then to a heat treatment. CONSTITUTION: The ceramic frit and 0.05 to 0.1 wt.% polymethylhydr...
|
|
JPH02240283A |
PURPOSE: To easily form a repairing layer having excellent adhesion and resistance to chemicals and infiltration when the glass layer of a glass-lined metallic device is broken by applying a repairing agent consisting of the phosphate-ba...
|
|
JPH02240281A |
PURPOSE: To stably produce an enameled substrate uniform in film thickness of enamel frit in the case of producing enameled substrates for an electronic circuits by fitting a substrate member made of a metallic sheet to a supporting fram...
|
|
JPH02236287A |
PURPOSE: To improve the thermal efficiency when a thermal head is adopted by providing the above base plate with insulating enamel layers having many pieces of the foam generated from a metallic salt. CONSTITUTION: For example, the metal...
|
|
JPH02232382A |
PURPOSE: To make flow production of high-temp. superconducting components by mounting ceramic materials onto supporting metals by an enamel coating technique. CONSTITUTION: The ceramic materials are mounted as high-temp. superconducting ...
|