Document |
Document Title |
JPH08258229A |
PURPOSE: To realize thermal lamination at low temperature, and facilitate embossing by a structure wherein the laminated film has the specified vinyl chloride copolymer composition layer and polyalcohol layer, which is obtained by reduci...
|
JPH08253676A |
PURPOSE: To obtain a resin composition, comprising specific amounts of a polyalcohol and an inorganic filler, having high gas barrier properties and excellent in processability without causing any pinhole, crack and local uneven wall thi...
|
JPH08253675A |
PURPOSE: To obtain the subject composition, comprising a specific polyvinyl alcohol and polysaccharides, excellent in easy decomposability and spreadability in forming a film, rapidly decomposing the molding thereof with microorganisms b...
|
JPH08244180A |
PURPOSE: To improve the gas barrier properties and the moistureproofness over the entire moisture area by providing a vinylidene chloride copolymer thin layer at least on one side surface of a polyalcohol obtained by reducing a polyketon...
|
JPH08245834A |
To improve the stability of an org. material to thermal, oxidative, and light-induced degradation by incorporating a stabilizer comprising two specific high-molecular polyalkylpiperidine derivs. into the material. The stabilizer mixture ...
|
JP2527348B2 |
|
JPH08208925A |
PURPOSE: To obtain a decorative vinyl chloride sheet markedly excellent in both low-smoking properties and low-hydrogen-chloride-gas-forming properties without detriment to flame retardancy conventionally controversial to these propertie...
|
JPH08208975A |
To obtain an alternating polyketone polymer compsn. stabilized against thermal oxidation by compounding a specific alternating polyketone polymer with specific antioxidants and a scavenger. A major amt. of an alternating polyketone polym...
|
JP2518735B2 |
|
JP2517635B2 |
|
JP2516996B2 |
|
JPH08176377A |
PURPOSE: To obtain a flame-retardant resin composition suitable for injection molding, providing a molded article having excellent impact resistance and external appearance, by adding a specific amount of an ethylene/carbon monoxide/(met...
|
JPH08176386A |
PURPOSE: To obtain a vinyl chloride-based resin composition providing a molded article having excellent flame retardance, impact resistance and heat resistance, comprising a vinyl chloride-based resin having a specific chlorine content, ...
|
JPH08176430A |
PURPOSE: To obtain a high-strength and highly heat-resistant resin composition excellent in melt flow stability. CONSTITUTION: This composition comprises 100 pts.wt. resin composition comprising 99-5 pts.wt. thermoplastic polyimide resin...
|
JPH08176353A |
PURPOSE: To obtain a thermoplastic elastomer remarkably improved in low- temperature impact and surface scuff resistances while maintaining the mechanical strength without deteriorating the surface scuff resistance and surface appearance...
|
JP2512450B2 |
|
JPH08505899A |
Dense star polymers or dendrimers having a highly branched interior structure capable of associating or chelating with metal ions are modified by capping with a hydrophobic group capable of providing a hydrophobic outer shell. The modifi...
|
JP2507778B2 |
A polymer composition comprising (a) 35-65 parts by weight polyvinyl chloride, (b) 10-55 parts by weight chlorinated polyethylene or chlorosulfonated polyethylene elastomer or mixtures thereof containing 24-40 weight percent chlorine, (c...
|
JP2509196B2 |
|
JPH08143768A |
PURPOSE: To obtain a thermoplastic resin compsn. which has a good flowability in molding and gives a molded item excellent in heat distortion resistance, impact strength, and appearance. CONSTITUTION: This resin compsn. comprises 5-95 pt...
|
JPH08134347A |
PURPOSE: To obtain a composition, excellent in especially light discoloration resistance, molding fluidity, appearance of moldings and impact resistance as compared with a conventional material and useful for automotive, electrical and e...
|
JPH08120134A |
PURPOSE: To obtain the subject composition having excellent sliding property and useful as a material for electrical and electronic parts such as housing of OA equipments by adding a polydimethylsiloxane having extremely decreased oligom...
|
JPH08503502A |
Compositions of coreactant resins, such as an epoxy resin, and polyanhydrides that contain non-cyclic anhydride moieties are cured to provide coatings that have good exterior durability. Preferred high molecular weight polyanhydrides con...
|
JPH0832826B2 |
|
JPH0881272A |
To obtain a binder for ceramic materials which remarkably shortens the purging time without a danger of suffering from deformation or fracture of green body by compounding a polyamide, stryrene copolymer and low molecular weight flow acc...
|
JPH0826199B2 |
|
JPH0826197B2 |
A curable polymeric composition exhibiting good low temperature flexibility comprising about 50-90 parts by weight chlorinated polyethylene or chlorosulfonated polyethylene containing about 30-45 weight percent chlorine, and about 10-50 ...
|
JPH0867812A |
To obtain a molding material based on a specified polyarylene ether and a specified copolyamide, having high toughness and high thermal shape stability and being excellent in processing stability. The objective material comprises (A) 1-9...
|
JPH0867814A |
PURPOSE: To obtain a resin composition excellent in the adhesivity to various plastic materials, scratch resistance, chemical resistance and yellowing weatherability. CONSTITUTION: This resin composition comprises (A) a polyurethane resi...
|
JPH0859901A |
To obtain a reinforced flame-resistant thermoplastic compsn. which is excellent in mechanical properties, processibility, and operation stability and does not form a toxic combustion product by compounding an olefinic or styrenic (co)pol...
|
JPH0853585A |
PURPOSE: To provide polymer blends comprising a polyketone and a PE, particularly a high density PE which are excellent in water barrier properties and useful for packaging applications. CONSTITUTION: Desired polymer blends comprise (A) ...
|
JPH0813925B2 |
|
JPH0841317A |
PURPOSE: To provide an extensible film which comprises a thermoplastic polyurethane resin compsn. has excellent high-speed hot-melt adhesion, excellent extensibility under low stress, low extension permanent set, and adequate strength an...
|
JPH0812487B2 |
|
JPH0834892A |
PURPOSE: To obtain a PVC article, especially, rigid one, having a high softening point and good physical properties by blending a specified polyketone with PVC. CONSTITUTION: A composition is made by blending (A) a polyketone being a lin...
|
JPH0834919A |
PURPOSE: To obtain a resin composition excellent in mechanical characteristics, heat resistance and moldability and useful as automotive parts, etc., by compounding a polyamide resin with a specific PS thermoplastic resin mixture in a sp...
|
JPH082999B2 |
|
JPH083012B2 |
|
JPH083011B2 |
|
JPH083018B2 |
|
JPH0812868A |
PURPOSE: To obtain a thermoplastic composition excellent in flame retardancy, resistance to shock and heat and moldability by formulating a fluororesin, a silicone and a specific a phosphoric ester to a composition of an aromatic polycar...
|
JPH07119343B2 |
|
JPH07119344B2 |
|
JPH07119342B2 |
|
JPH07331073A |
PURPOSE: To obtain the subject mixture comprising a polysiloxane, a reactive filler, and a pigment, which fully cures at room temperature to form a water- repellent coating material and is useful for coating building materials and facade...
|
JPH07116354B2 |
|
JPH07316370A |
PURPOSE: To obtain a molded product good in the surface property and excellent in thermal deformation resistance, impact resistance and oil resistance because of being extremely little in the staining of a mold. CONSTITUTION: In the meth...
|
JPH07103305B2 |
A polycarbonate blend of good impact strength, solvent resistance and weldline properties is prepared by admixing polycarbonate, a grafted olefin/carbon monoxide copolymer and optionally a styrenic component such as ABS and/or an aromati...
|
JPH07292192A |
PURPOSE: To obtain the subject composition good in transparency, mechanical strength, fluidity, etc., by dispersing a rubbery component and incorporating an organopolysiloxane compound in a continuous matrix resin prepared by copolymeriz...
|
JPH07292189A |
PURPOSE: To provide a transparent molding material having a satisfactory notched impact strength which comprises a methyl methacrylate polymer, a styrene-acrylonitrile polymer, a certain polysiloxane and a certain graft copolymer at a sp...
|