WO/2014/206521A1 |
The invention relates to a method for producing an impeller of an exhaust gas turbocharger from a TiAI-alloy (3). According to the invention, the alloy (3) has at least 1,9 at/% niobium and the impeller is formed by centrifugal casting t...
|
WO/2014/201476A1 |
A metering unit (14) for molten lead is paired with the molding cavity (13) of a molding block (6). The metering unit (14) comprises a cylinder (1), to which molten lead is supplied via a blockable line (8), and a piston (2), which can b...
|
WO/2014/202157A1 |
A furnace (10) for non-iron metals and a method of operating it are disclosed with a monitoring system (12) for monitoring in-situ the concentration of a passivation fluid,such as perfluoroketones in a cover gas(136). The monitoring syst...
|
WO/2014/171548A1 |
The present invention pertains to a production method for a fire-resistant magnesium alloy having the mechanical characteristics of a long-period stacked magnesium alloy and having an ignition temperature of at least 800°C. The fire-res...
|
WO/2014/171549A1 |
The present invention pertains to a production method for a fire-resistant magnesium alloy having the mechanical characteristics of a long-period stacked magnesium alloy and having an ignition temperature of at least 800°C. The producti...
|
WO/2014/170946A1 |
Provided is a production method for an Al-Mg-Si-based aluminium alloy member for resin bonding, said method being suitable for producing, by bonding a resin moulded body to a surface of the Al-Mg-Si-based aluminium alloy member, an alumi...
|
WO/2014/170945A1 |
The purpose of the present invention is to provide: a production method for an aluminium casting-alloy member for resin bonding, said method being capable of producing, with ease by way of a simple method, an aluminium casting-alloy memb...
|
WO/2014/168183A1 |
Provided is a method for producing a zinc alloy, which enables the production of a Zn-Si alloy having a uniform composition. Metal Zn is melted in a crucible (2) arranged in a heating furnace (1) to produce molten Zn (4). The floating of...
|
WO/2014/163089A1 |
A titanium slab for hot rolling, made from an industrial pure titanium, wherein a structural refinement layer comprising an acicular structure is present on the outermost surface of the surface representing the rolling surface, an inside...
|
WO/2014/163087A1 |
A surface to be rolled of a titanium cast piece, which comprises industrial pure titanium produced by an electron beam melting method or a plasma arc melting method, is melted together with a material containing a β-phase-stabilizing el...
|
WO/2014/136535A1 |
A cylinder head body (100) constituting part of an air-cooled, single-cylinder internal combustion engine and integrally formed from an aluminum alloy by die-casting, wherein the aluminum alloy contains 8.0-12.0 wt%, inclusive, of Si, 0....
|
WO/2014/130088A1 |
New magnesium-zinc aluminum alloy bodies and methods of producing the same are disclosed. The new magnesium-zinc aluminum alloy bodies generally include 3.0 - 6.0 wt. % magnesium and 2.5 - 5.0 wt. % zinc, where at least one of the magnes...
|
WO/2014/115794A1 |
Provided are: a metal glass casting device which can also be used in cases in which the metal glass casting mold is subjected to difficult conditions; and a casting method using said device. The metal glass casting device comprises: a ...
|
WO/2014/112151A1 |
The present invention relates to an alloy that is mainly composed of Mo, Si, B, Ti, at least one of Zr and Hf, and at least one of C and N. The present invention also relates to a method for producing an alloy that is mainly composed of ...
|
WO/2014/109624A1 |
An aluminum alloy for die casting according to the present invention comprises 8.5-10.5 wt% of silicon (Si), 2.0-3.7 wt% of copper (Cu), 1.0 wt% or less of iron (Fe), 1.0-5.0 wt% of zinc (Zn), 0.6-1.0 wt% of magnesium (Mg), 0.4 wt% or le...
|
WO/2014/106989A1 |
The present invention relates to a method for manufacturing an extruded magnesium alloy and an extruded magnesium alloy manufactured thereby. The present invention specifically relates to a method for manufacturing an extruded magnesium ...
|
WO/2014/091939A1 |
Provided is a method for producing a silicon-containing aluminum alloy ingot with which it is possible to prevent filter clogging that requires the suspension of casting, to suppress aluminum loss, and to reduce the content by percentage...
|
WO/2014/091936A1 |
Provided is a method for producing a silicon-containing aluminum alloy ingot with which it is possible to prevent filter clogging that requires the suspension of casting, to suppress aluminum loss, and to reduce the content by percentage...
|
WO/2014/077653A1 |
The present invention provides a zinc alloy with improved alloy characteristics such as fluidity, castability, mechanical properties, corrosion resistance and elongation, and a preparation method therefor. The method for preparing the zi...
|
WO/2014/077203A1 |
Provided is a sand for a casting mold that includes sand (1), a binder (2), and inorganic compound particles (3) that are water insoluble and generate a gas (4A) (at least one of steam and carbon dioxide gas) due to the heat of molten me...
|
WO/2014/076174A1 |
A method is described for producing an engine component, more particularly a piston for an internal combustion engine, in which an aluminium alloy is cast using the gravity die casting method and wherein the aluminium alloy comprises the...
|
WO/2014/069936A1 |
The present invention relates to a method for preparing a recycled low-nickel magnesium alloy using magnesium scraps. More particularly, the recycled magnesium alloy having a reduced nickel content can be prepared by adding Al and misch ...
|
WO/2014/065626A1 |
The present invention relates to a method for manufacturing a bearing insert for a lower crank case of an engine. The method of the present invention, comprises: a molten metal preparation step of melting an aluminum alloy composition so...
|
WO/2014/061329A1 |
Provided are a vehicular component and a vehicular aluminum alloy for which toughness appropriate for a vehicle component can be secured even when using an aluminum material containing impurities such as Fe and Cu. The vehicular aluminum...
|
WO/2014/050815A1 |
Provided are a hypereutectic aluminum/silicon alloy die-cast member which contains 20.0-30.0 mass% silicon and has a thickness of 2.5 mm or less and a process for producing the die-cast member. The die-cast member is characterized by bei...
|
WO/2014/045475A1 |
A cooling method comprises: a product-side showering step of showering a mist of liquid for cooling on a first face of an Al alloy manufactured casting (10) which comprises a product (11) and a riser (12) (the first face being a face on ...
|
WO/2014/038802A1 |
The present invention provides a method for preparing an aluminum matrix composite by infiltrating aluminum into a preform within a short time even without pressurization by using a special apparatus compared with a conventional pressure...
|
WO/2014/038333A1 |
This process comprises steps (S1 to S4) for forming an aluminum alloy casting, a step (S6) for subjecting the casting which has been taken out of a mold to cooling with a cooling fluid, and a step (S10) for subjecting the cooled casting ...
|
WO/2014/035602A1 |
The disclosure relates generally to mold compositions comprising calcium aluminate and calcium titanate. The disclosure also relates to methods of molding and the articles so molded using the mold compositions. More specifically, the dis...
|
WO/2014/030915A1 |
The present invention relates to an aluminum alloy for die casting which can obtain excellent thermal conductivity while simultaneously having a remarkable casting property and satisfactory tensile characteristics, and thus can be applie...
|
WO/2014/010757A1 |
The present invention in one aspect provides a method for removing inclusions 300 μm or larger in diameter contained in molten metal of a magnesium alloy, through filtration the molten metal by a filter for filtration having a plurality...
|
WO/2013/187308A1 |
An aluminum alloy plate according to one aspect of the present invention contains a peritectic element and Mg. Concerning the concentration of the peritectic element, the difference between the concentration in the thickness center part ...
|
WO/2013/187671A1 |
The present invention includes a first injection tube for supplying a colloidal medium, a storage part connected to the first injection tube for receiving the colloidal medium through the first injection tube, a second injection tube con...
|
WO/2013/172912A2 |
New Al-Li alloy bodies and methods of producing the same are disclosed. The new Al-Li alloy bodies may be produced by preparing the aluminum alloy body for post-solutionizing cold work, cold working by at least 25%, and then thermally tr...
|
WO/2013/172910A2 |
New 2xxx aluminum alloy bodies and methods of producing the same are disclosed. The new 2xxx aluminum alloy bodies may be produced by preparing the aluminum alloy body for post-solutionizing cold work, cold working by at least 25%, and t...
|
WO/2013/165070A1 |
The present invention relates to a method for manufacturing a wheel hub for a wide commercial vehicle, more specifically to a method for manufacturing a wheel hub, for a wide commercial vehicle, which is coupled to a single wheel-type wh...
|
WO/2013/165068A1 |
The present invention relates to a wheel for a wide commercial vehicle and a method for manufacturing same, more specifically to a new single wheel-type wheel for a wide commercial vehicle having a single rim part and a single hub formed...
|
WO/2013/157903A1 |
The aim of the present invention is to provide a method for manufacturing an aluminum alloy using, as a source of calcium and silicon to be added to aluminum, a calcium-based additive and a silicon-based additive which are more chemicall...
|
WO/2013/157376A1 |
Provided is a magnesium alloy member that satisfies elongation requirements and 0.2% proof stress at the same time so as to have excellent strength and workability while having further strength and compressive residual stress near the su...
|
WO/2013/150700A1 |
Provided are: an aluminum alloy for a die cast, which is highly safe, rarely undergoes casting cracking and can have a reduced thickness in spite of a simple formulation thereof, has seizure resistance, fluidability and a property of bei...
|
WO/2013/137095A1 |
This aluminum alloy is configured to be composed of 10.5-13% by mass of Si, 1.5-3% by mass of Ni, 2-5.5% by mass of Cu, 0.1-0.6% by mass of Mg, 0-0.25% by mass of Fe, 0.002-0.02% by mass of P, 0.05-0.3% by mass of Ti, 0.05-0.2% by mass o...
|
WO/2013/133978A1 |
New HT aluminum alloy bodies and methods of producing the same are disclosed. The new HT aluminum alloy bodies contain 0.20 - 2.0 wt. % Mg, 0.10 - 1.5 wt. % Si, 0.01 - 1.0 wt. % Fe, and, 0.10 - 1.0 wt. % Cu, wherein, when Si+Cu < 0.60 wt...
|
WO/2013/133976A1 |
New 6xxx aluminum alloy bodies and methods of producing the same are disclosed. The new 6xxx aluminum alloy bodies may be produced by preparing the aluminum alloy body for post-solutionizing cold work, cold working by at least 25%, and t...
|
WO/2013/133960A1 |
New 7xxx aluminum alloy bodies and methods of producing the same are disclosed. The new 7xxx aluminum alloy bodies may be produced by preparing the aluminum alloy body for post-solutionizing cold work, cold working by at least 25%, and t...
|
WO/2013/129012A1 |
Provided is a method for molding an amorphous alloy, the method having a high degree of processing freedom regardless of the components of the amorphous alloy, which especially is a metallic glass, and of the shape of the article to be m...
|
WO/2013/122069A1 |
High-purity titanium ingots with a purity of at least 99.99% by mass, excluding added elements and gas components. Said titanium ingots are characterized by containing an added component consisting of a total of 0.1 to 100 ppm by mass of...
|
WO/2013/115490A1 |
The present invention relates to a magnesium alloy having high ductility and high toughness, and a preparation method thereof, and more specifically, to: a magnesium alloy having high ductility and high toughness, comprising 1.0-3.5 wt% ...
|
WO/2013/114928A1 |
Provided is a forged aluminum alloy material which contains an excess of Si, which exhibits increased strength due to containing therein a large quantity of a strength-increasing element such as Cu or Mn, and by which high strength and h...
|
WO/2013/105831A1 |
The present invention relates to an aluminum alloy for die casting which can have excellent thermal conductivity while having excellent casting property and satisfactory mechanical properties, and thus can be applied to various structura...
|
WO/2013/100427A1 |
The present invention provides a magnesium deactivating agent to be added for improving the flame retardancy and corrosion resistance of magnesium and a magnesium alloy, and more particularly, a magnesium deactivating agent which forms a...
|